ASTM A268 TP430 Ferritic Stainless Steel Seamless Pipes
We are one of the biggest manufactures of stainless steel & duplex steel & alloy steel tubes and pipes in China. With development more than 20 years, we have accumulated a great many clients all around the world and Yuhong products also won the great praise among the customers.
ASTM A268 is Standard specification for Seamless and Welded Ferritic and Martensitic Stainless Steel Tubing for General Service, the grades contain TP410, TP405, TP420, TP430, TP430Ti, TP403, TP409, TP444, TP439 and TP446, it covers standard specification for a number of grades of nominal-wall-thickness, welded ferritic and martensitic stainless steel tubing for general corrosion-resisting and high-temperature service, ASME SA268 is alternative standard.
The tubes shall be made by the seamless or welded process with no filler metal added, tubes shall be reheated to a temperature of 1200.F [650.C] or higher and cooled to meet the requirements of this specification, All tubes shall be free of excessive mill scale, suitable for inspection. A slight amount of oxidation will not be considered as scale.
ASTM A268 Chemical Composition
| Grade: | TP410 | TP430 | TP439 |
| UNS | S41000 | S43000 | S43035 |
| C, Max | 0.15 | 0.12 | 0.07 |
| Mn,Max | 1 | 1 | 1 |
| P, Max | 0.04 | 0.04 | 0.04 |
| S, Max | 0.03 | 0.03 | 0.03 |
| Si, Max | 1 | 1 | 1 |
| Ni | … | … | 0.50max |
| Cr | 11.5-13.5 | 16.0-18.0 | 17.00-19.00 |
| Mo | … | … | … |
| Al | … | … | 0.15 |
| Cu | … | … | … |
| N | … | … | 0.04 |
| Ti | … | … | 0.20+4(C+N)Min, 1.10max |
ASTM A268 Mechanical Properties
| Grade | Tensile Strength, Min, Ksi [MPa] | Yield Strength, Min, Ksi [MPa] | ELONGATION. MIN, % |
| TP410 | 55 [380] | 30 [205] | 20 |
| TP430 | 60 [415] | 35 [240] | 20 |
| TP439 | 60 [415] | 30 [205] | 20 |
ASTM A268 TP430 Physical Properties
| Density, g/cm3 (lb/in.3) | 7.8 (0.28) |
| Melting point, °C (°F) | 1425-1510 (2600-2750) |
| Specific heat capacity, J/kg · K (Btu/lb · °F) | 460 (0.11) at 0-100 °C (32 to 212 °F) |
| Electrical resistivity, μΩ·m | 0.60 at 20 ℃ |
| 430 stainless steel magnetic permeability | 600-1100 (Approximate) |
| Elastic modulus (Modulus of elasticity), GPa (106 psi) | 200 (29.0) |
| Thermal diffusivity, mm2/s | 7.3 |
| Thermal conductivity, W/m · K (Btu/ft · h · °F) | 26.1 (15.1), at 100 ℃ (212 °F) |
| 26.3 (15.2), at 500 ℃ (932 °F) | |
| Coefficient of thermal expansion, μm/m · °C (μin./in. · °F) | 10.4 (5.8), at 0-100 ℃ (32-212 °F) |
| 11.0 (6.1), at 0-315 ℃ (32-600 °F) | |
| 11.4 (6.3), at 0-538 ℃ (32-1000 °F) |
SS430 Stainless Steel Heat Treatment
Heat Resistance
| Maximum service temperatures, °C (°F) | ||
| AISI | Intermittent service | Continuous service |
| 430 | 870 (1600) | 815 (1500) |
SS430 Stainless Steel Applications